Effect of Surface State on Steam Oxidation Rate of Steel TP347H

ZHANG Bo, QI An-fang, JIN Yong-qiang, WANG Jian-yong,ZHENG Zi-jie, ZHENG Kai-yun

Journal of Chinese Society of Power Engineering ›› 2012, Vol. 32 ›› Issue (11) : 903-908.
Material Science

Effect of Surface State on Steam Oxidation Rate of Steel TP347H

  • ZHANG Bo1, QI An-fang1, JIN Yong-qiang1, WANG Jian-yong1,ZHENG Zi-jie1, ZHENG Kai-yun2
Author information +
History +

Abstract

Steam oxidation tests were carried out at 650 ℃ for 2 000 hours in steam oxidation furnace for TP347H specimens with surfaces respectively treated by grinding, shot blasting, fine grain + acid pickling, grinding + acid pickling and 15% cold deforming + acid pickling, so as to analyze the influence of the surface state on the oxidation rate, during which the surface morphology and composition of oxidized specimens were observed and studied using SEM and EDS, while the oxidation film analyzed using XRD, and the oxidation rate calculated by weight loss and thickness method. Results show that the oxidation films formed on above five specimens have basically similar morphology, but their oxidation rates are different, which are found to be in following increasing order: grinding, shot blasting, fine grain + acid pickling, grinding + acid pickling and 15% cold deforming + acid pickling specimen.

Key words

TP347H steel / steam oxidation / surface state / oxide film morphology / oxidation rate

Cite this article

Download Citations
ZHANG Bo, QI An-fang, JIN Yong-qiang, WANG Jian-yong,ZHENG Zi-jie, ZHENG Kai-yun. Effect of Surface State on Steam Oxidation Rate of Steel TP347H. Journal of Chinese Society of Power Engineering. 2012, 32(11): 903-908

References

[1] 赵慧传,贾建民,陈吉刚,等.超临界锅炉末级过热器爆管原因的分析[J].动力工程学报,2011,31(1):69-74.
ZHAO Huichuan, JIA Jianmin, CHEN Jigang, et al.Burst cause analysis of final-stage superheater tuber for a supercritcal boiler[J].Journal of Chinese Society of Power Engineering,2011,31(1):69-74.
[2] 王殿仲,徐宪龙.630 MW 超临界锅炉高温受热面氧化皮形成及脱落原因分析[J].电力设备,2008,19(3):45-47.
WANG Dianzhong, XU Xianlong. Cause analysis of scale formation and fall-off from high temperature heat surfaces of 630 MW supercritical boilers[J]. Electrical Equipment, 2008,19(3):45-47.
[3] 银龙,宋寿春,毕法森,等.超超临界机组氧化皮的产生与防范[J].电力设备,2006,7(10):33-36.
YIN Long, SONG Shouchun, BI Fasen, et al. Iron scale production and prevention of supercritical pressure boiler[J].Electrical Equipment,2006,7(10):33-36.
[4] 胡庚祥,钱苗根.金属学[M].上海:上海科学技术出版社,1980: 115-116.
[5] 王建泳,张波,金用强,等.奥氏体钢管内壁喷丸特性及其对抗氧化性能的影响[J].锅炉技术,2009,40(2):48-51.
WANG Jianyong, ZHANG Bo, JIN Yongqiang, et al. The characteristics of internal surface treated by shot blasting and its effectic stainless steel tube[J]. Boiler Technology,2009,40(2):48-51.

646

Accesses

0

Citation

Detail

Sections
Recommended

/