蒸汽侧氧化膜对锅炉T91钢管蠕变断裂寿命的影响

动力工程学报 ›› 2013, Vol. 33 ›› Issue (8) : 659-664.

材料科学

边彩霞¹, 周克毅², 朱正林¹, 胥建群²

作者信息 +

Effects of Steam-side Oxide Scale on Creep Rupture Lifeof T91 Boiler Steel Tubes

BIAN Caixia¹, ZHOU Keyi², ZHU Zhenglin¹, XU Jianqun²

Author information +

History +

摘要

建立了电站锅炉T91钢管蠕变断裂寿命计算模型,定量分析了蒸汽侧管壁温度和等效应力对T91受热管蠕变断裂寿命的影响,并对不同热负荷、不同尺寸受热管的计算结果进行了比较.结果表明:蒸汽侧氧化膜导致管壁温度升高是缩短部件蠕变断裂寿命的主要原因,等效应力增大是次要原因;受热管的蠕变断裂寿命随蒸汽侧氧化膜厚度的增加呈抛物线缩短;随管子热负荷的增加,蒸汽侧氧化膜对受热管蠕变断裂寿命的影响程度加剧;蒸汽侧氧化膜对外径较小的厚壁管子蠕变断裂寿命的影响较大.

Abstract

A calculation model was built up for the creep rupture life of T91 steel tubes, with which the effects of steam-side oxide scale on the creep rupture life were analyzed quantitatively from the aspects of temperature and equivalent stress, while a comparison made to the calculation results obtained under different conditions of heat flux and tube size. Results show that the increase of metal temperature resulted from steam-side oxide scale is the main cause of creep rupture life reduction, and the rise of equivalent stress is the secondary one; a parabolic relationship exists between the reduction of creep rupture life and the thickness of steam-side oxide scale; the effect of steam-side oxide scale on the creep rupture life intensifies with the rise of heat flux; the steam-side oxide scale has greater influence on creep rupture life of tubes with smaller outside diameter but larger wall thickness.

导出引用

边彩霞, 周克毅, 朱正林, 胥建群. 蒸汽侧氧化膜对锅炉T91钢管蠕变断裂寿命的影响. 动力工程学报. 2013, 33(8): 659-664

BIAN Caixia, ZHOU Keyi, ZHU Zhenglin, XU Jianqun. Effects of Steam-side Oxide Scale on Creep Rupture Lifeof T91 Boiler Steel Tubes. Journal of Chinese Society of Power Engineering. 2013, 33(8): 659-664

参考文献

[1] ARMITT J,HOLMS D R,MANNING M I,et al.The spalling of steam grown oxide from superheater and reheater tube steels[R].California, USA:Electric Power Research Institute,1978.
[2] DOOLEY R B, WRIGHT I G, TORTORELLI P F,et al. Program on technology innovation: oxide growth and exfoliation on alloys exposed to steam[R]. California, USA:Electric Power Research Institute,2007.
[3] 贾建民,陈吉刚,唐丽英,等.12X18H12T钢管蒸汽侧氧化皮及其剥落物的微观结构与形貌特征[J].中国电机工程学报,2008,28(17):44-48.
JIA Jianmin,CHEN Jigang,TANG Liying,et al.Investigation on microstructure and morphology features of steam-side oxidation scale and exfoliated oxide from the internal surface of 12X18H12T tube[J].Proceedings of the CSEE,2008,28(17):44-48.
[4] 赵慧传, 贾建民, 陈吉刚,等. 超临界锅炉末级过热器爆管原因的分析[J]. 动力工程学报, 2011, 31(1): 69-74.
ZHAO Huichuan, JIA Jianmin, CHEN Jigang, et al. Burst cause analysis of final-stage superheater tubes for a supercritical boiler[J].Journal of Chinese Society of Power Engineering, 2011, 31(1): 69-74.
[5] 边彩霞,周克毅,胥建群,等. 蒸汽侧氧化膜对超临界机组T92钢管壁温的影响[J]. 动力工程, 2009, 29(5): 502-506.
BIAN Caixia, ZHOU Keyi, XU Jianqun, et al. Influence of steam-side oxide scale on wall temperature of T92 tubes for supercritical units[J]. Journal of Power Engineering, 2009, 29(5): 502-506.
[6] 林俊滨. 超(超)临界锅炉高温管内氧化皮形成机理及堵塞规律研究[D]. 广州:华南理工大学,2010.
[7] 唐海宁. 大容量电站锅炉金属氧化皮问题综合分析[D]. 南京:东南大学,2006.
[8] MONTGOMERY M, HANSSON A N, VILHELMSEN T, et al. Steam oxidation of X20CrMoV121: comparison of laboratory exposures and in situ exposure in power plants[J]. Materials and Corrosion, 2012, 63(8):674-684.
[9] TAN L, REN X, ALLEN T R. Corrosion behavior of 9%-12% Cr ferritic-martensitic steels in supercritical water[J]. Corrosion Science, 2010, 52(4): 1520-1528.
[10] 张都清. 电站9Cr-1Mo-V-Nb钢高温氧化机制及防护技术研究[D]. 济南:山东大学, 2009.
[11] NICKEL H, ENNIS P J, QUADAKKERS W J. The creep rupture properties of 9% Chromium steels and the influence of oxidation on strength[J]. Mineral Processing and Extractive Metallurgy Review, 2001, 22(1): 181-195.
[12] VISWANATHAN R, SARVER J, TANZOSH J M. Boiler materials for ultra-supercritical coal power plants-steamside oxidation[J]. Journal of Materials Engineering and Performance, 2006, 15(3): 255-274.
[13] NISHIMURA N, KOMAI N, HIRAYAMA Y, et al. Japanese experience with steam oxidation of advanded heat-resistant steel tubes in power boilers[J]. Materials at High Temperatures, 2005, 22 (1/2): 3-10.
[14] DIONISIO L, TOMOMS G A, FRANCISCO C. Continuous and cyclic oxidation of T91 ferritic steel under steam[J]. Corrosion Science, 2004, 46 (3): 613-631.
[15] CHEN Y, SRIDHARAN K S, TODD A. Corrosion behavior of ferritic-martensitic steel T91 in supercritical water[J]. Corrosion Science, 2006, 48(9): 2843-2854.
[16] CIPOLLA L, GABREL J. New creep rupture assessment of Grade 91[C]//Proceedings of the First International Conference on Super-high Strength Steels. Rome, Italy: AIM, 2005.
[17] 徐芝纶. 弹性力学[M].北京:高等教育出版社,2006.
[18] 吕邦泰, 沈月芬. 锅炉承压部件强度及寿命[M]. 北京:水利电力出版社,1992.
[19] 李之光. 锅炉受压原件强度标准分析[M]. 北京:技术标准出版社,1980.
[20] RAY A K, TIWARI Y N, SINHA R K, et al. Residual life prediction of service exposed main steam pipe of boilers in a thermal power plant[J]. Engine-ering Failure Analysis, 2000, 7(5): 359-376.

基金

南京工程学院校级科研基金资助项目(YKJ201211);国家自然科学基金资助项目(51176031)

523

Accesses

Citation

Detail

段落导航

摘要
Abstract
关键词
Key words
引用本文
参考文献
基金

Received	Published
2012-08-17	2013-08-25
Issue Date
2013-08-25

选择文件类型/文献管理软件名称

选择包含的内容

摘要

Abstract

关键词

Key words

引用本文

{{custom_sec.title}}

{{custom_sec.title}}

参考文献

{{custom_fnGroup.title_cn}}

脚注

基金